Method of treatment subterranean formations using multiple proppant stages or mixed proppants

ABSTRACT

An increase in effective propped lengths is evidenced in hydraulic fracturing treatments by the use of ultra lightweight (ULW) proppants. The ULW proppants have a density less than or equal to 2.45 g/cc and may be used as a mixture in a first proppant stage wherein at least one of the proppants is a ULW proppant. Alternatively, sequential proppant stages may be introduced into the formation wherein at least one of the proppant stages contain a ULW proppant and where at least one of the following conditions prevails:
         (i.) the density differential between the first proppant stage and the second proppant stage is greater than or equal to 0.2 g/cc;   (ii.) both the first proppant stage and the second proppant stage contain a ULW proppant;   (iii.) the rate of injection of the second proppant stage into the fracture is different from the rate of injection of the first proppant stage; or   (iv.) the particle size of the second proppant stage is different from the particle size of the first proppant stage.

This application claims the benefit of U.S. application Ser. Nos.60/455,717, filed on Mar. 18, 2003 and 60/508,822, filed Oct. 3, 2003,which are herein incorporated by reference.

FIELD OF THE INVENTION

This invention relates to a method of treating subterranean formationsand, more specifically, to hydraulic fracturing treatments forsubterranean formations. Use of the method of the invention renders anincrease in effective propped lengths by as much as 100%. Thus, theinventive method increases well productivity, greatly enhances reservoirdrainage, and improves hydrocarbon recovery.

BACKGROUND OF THE INVENTION

Hydraulic fracturing is a common stimulation technique used to enhanceproduction of fluids from subterranean formations. Hydraulic fracturingis typically employed to stimulate wells which produce from lowpermeability formations. In such wells, recovery efficiency is typicallylimited by the flow mechanisms associated with a low permeabilityformation.

During hydraulic fracturing, a viscosified fracturing fluid is pumped athigh pressures and at high rates into a wellbore to initiate andpropagate a hydraulic fracture. Once the natural reservoir pressures areexceeded, the fluid induces a fracture in the formation and transportsthe proppant into the fracture. The fluid used to initiate and propagatethe fracture is commonly known as the “pad”. The pad may contain a heavydensity fine particulate, such as fine mesh sand, for fluid losscontrol, or larger grain sand to abrade perforations or near-wellboretortuosity. Once the fracture is initiated, subsequent stages ofviscosified fracturing fluid containing chemical agents such asbreakers, and containing proppants are pumped into the created fracture.The fracture generally continues to grow during pumping and the proppantremains in the fracture in the form of a permeable “pack” that serves to“prop” the fracture open. Once the treatment is completed, the fracturecloses onto the proppants which maintain the fracture open, providing ahighly conductive pathway for hydrocarbons and/or other formation fluidsto flow into the wellbore. The fracturing fluid ultimately “leaks off”into the surrounding formation. The treatment design generally requiresthe fracturing fluid to reach maximum viscosity as it enters thefracture which affects the fracture length and width.

Fracturing fluids, including those containing breakers, typicallyexhibit poor transport properties. High pumping rates are required inorder to impart a sufficient velocity for placement of the proppant inthe fracture. In such treatments, the proppant tends to settle, forminga ‘proppant bank’, as the linear slurry velocity falls as a function ofthe distance from the wellbore. This effect is further believed toresult in reduced stimulation efficiency as the effective propped lengthis relatively short. In addition, much of the settled proppant is oftenbelow the productive interval.

The recovery of the fracturing fluid is accomplished by reducing theviscosity of the fluid to a low value such that it flows naturally fromthe formation under the influence of formation fluids and pressure. Thisviscosity reduction or conversion is referred to as “breaking”.Historically, the application of breaking fluids as fracturing fluids atelevated temperatures, i.e., above about 120–130° F., has been acompromise between maintaining proppant transport and achieving thedesired fracture conductivity, measured in terms of effective proppedfracture length. Conventional oxidative breakers react rapidly atelevated temperatures, potentially leading to catastrophic loss ofproppant transport. Encapsulated oxidative breakers have experiencedlimited utility at elevated temperatures due to a tendency to releaseprematurely or to have been rendered ineffective through payloadself-degradation prior to release.

Improvements in hydraulic fracturing techniques are required in order toincrease the effective propped fracture length and thereby improvestimulation efficiency and well productivity.

SUMMARY OF THE INVENTION

The invention relates to a method of hydraulically fracturing ahydrocarbon-bearing subterranean formation by introducing into theformation one or more proppant stages wherein at least one of theproppant stages contains an ultra lightweight (ULW) proppant having adensity less than or equal to 2.45 g/cc. The method results in anincrease in the effective propped fracture length. The first proppantstage may consist of a mixture of proppants, at least one of which is anULW proppant having a density less than or equal to 2.45 g/cc.Alternatively, sequential proppant stages may be introduced into theformation wherein at least one of the proppant stages contains a ULWproppant.

The first proppant stage may be a pad fluid, containing a proppant, andpumped at a pressure sufficient to initiate a fracture. Alternatively,the first proppant stage may be pumped into a propagated fracture. Assuch, the first proppant stage of the invention may be introduced intothe fracture subsequent to propagation of the fracture. An optionalsecond proppant stage may be injected into the fracture afterintroduction of the first proppant stage. Successive proppant stages maybe injected into the fracture after injection of the optional secondproppant stage. The second proppant stage may be introduced into theformation immediately after the first proppant stage.

Thus, in the method of the invention, at least one of the followingconditions should prevail:

(i.) the first proppant stage contains a mixture of proppants—forexample, a first proppant and a second proppant—wherein at least one ofthe proppants is a ULW; preferably, the density differential between theULW proppant and the second proppant in the proppant mixture is greaterthan or equal to 0.2 g/cc. For instance, the first proppant stage maycontain a mixture of two proppants comprising a ULW proppant and anon-ULW proppant. In such proppant mixtures, the differential in thedensity between the two proppants is preferably greater than 0.2 g/cc.Alternatively, where the invention encompasses two or more proppantstages, all or some of the proppant stages may contain a mixture ofproppants, wherein within each proppant stage, at least one of theproppants is a ULW proppant. In each proppant stage, the density of theULW proppant within the mixture is preferably greater than or equal to0.2 g/cc the density of a second proppant within the mixture;

(ii.) the density differential between the first proppant stage and thesecond proppant stage is greater than or equal to 0.2 g/cc;

(iii.) the first proppant stage and the second proppant stage bothcontain ULW proppants;

(iv.) the proppant of the first proppant stage and/or the secondproppant stage is a ULW and the rate of injection of the second proppantstage into the fracture is different from the rate of injection of thefirst proppant stage; in a preferred mode, the rate of injection of thesecond proppant stage is less than the rate of injection of the firstproppant stage; or

(v.) the proppant of the first proppant stage and/or the second proppantstage contains a ULW proppant and the particle size of the secondproppant stage is different from the particle size of the first proppantstage; in a preferred mode, the particle size of the second proppantstage is preferably larger than the particle size of the proppant of thefirst proppant stage when the second proppant stage is directed moretowards the wellbore. The particle size of the second proppant stage ispreferably smaller than the particle size of the proppant of the firstproppant stage when the second proppant stage is directed further intothe fracture.

The effective propped length of the fracture after injection of anygiven proppant stage is preferably greater than the effective proppedlength of the proppant stage introduced into the fracture just prior tothe injection of the any given proppant stage.

In a preferred embodiment, the first proppant stage comprises a firstproppant and a second proppant, wherein the first proppant is arelatively high-density proppant, i.e., having a density greater than2.45 g/cc, such as sand, ceramic, sintered bauxite or resin coatedproppant, and the second proppant is a ULW proppant. A subsequent secondproppant stage may include an ultra-lightweight proppant, exhibiting aparticle density substantially lower than the density of the relativelyhigh-density proppant. For instance, the proppant of the subsequentproppant stage has a density less than or equal to 2.45 g/cc, preferablyranging between from about 1.25 g/cc to about 1.75 g/cc.

Additional proppant stages may be introduced into the formation afterintroduction of the second proppant stage. Such additional proppantstages will be referred to herein as the “ultimate proppant stage” andthe “penultimate proppant stage” to refer to the latter and next tolatter proppant stages, respectively. For example, where three proppantstages are employed and when referring to the third and second proppantstages, the third proppant stage may be referred to as the “ultimateproppant stage” and the second proppant stage as the “penultimateproppant stage.” Where four proppant stages are employed and whenreferring to the fourth and third proppant stages, the fourth proppantstage may be referred to as the “ultimate proppant stage” and the thirdproppant stage may be referred to as the “penultimate proppant stage,”etc. The ultimate proppant stage may be introduced into the formationimmediately after the penultimate proppant stage. At least one of thefollowing conditions preferably prevails:

(i.) the density differential between the ultimate proppant stage andthe penultimate proppant stage is greater than or equal to 0.2 g/cc; forinstance, when referring to the third and second proppant stages, thedensity differential between the third proppant stage and the secondstage is greater than or equal to 0.2 g/cc;

(ii.) the rate of injection of the ultimate proppant stage into thefracture is different from the rate of injection of the penultimateproppant stage; typically, the rate of injection of the ultimateproppant stage into the fracture is lower than the rate of injection ofthe penultimate proppant stage into the fracture; or

(iii.) the particle size of the ultimate proppant stage is differentfrom the particle size of the penultimate proppant stage; typically, theparticle size of the proppant of the ultimate proppant stage into thefracture is dependent on whether the proppant stage is directed moretowards the wellbore (generally larger) or further into the fracture(generally smaller).

In a preferred embodiment, the first proppant stage comprises a firstproppant and a second proppant, wherein the first proppant is arelatively high-density proppant, such as sand, ceramic, sinteredbauxite or resin coated proppant, and the second proppant has a densityless than or equal to 2.45 g/cc.

Alternatively, a fracture may be created in the formation by injecting abanking fluid containing a first proppant stage into the formation at apressure sufficient to allow the formation of a proppant bank. A secondproppant stage is then injected into the fracture. The proppant ofeither the first proppant stage or the second proppant stage or both maycontain a ULW proppant. In a preferred embodiment, the densitydifferential between the proppant of the first proppant stage (thebanking fluid) and the proppant of the second proppant stage is at least0.2 g/cc.

Alternatively, a fluid containing a relatively high-density proppant maybe used to propagate the fracture, allowing it to form the bank. Thesubsequent second proppant stage may include an ultra-lightweightproppant, exhibiting a particle density substantially lower than thedensity of the relatively high-density proppant. For instance, theproppant of the subsequent proppant stage may have a density rangingbetween from about 1.25 g/cc to about 1.75 g/cc.

The invention further has particular applicability in the use of a ULWproppant in a pad fluid to initiate a fracture in the formation. Thesecond proppant stage introduced into the fracture may contain a ULWproppant or a proppant of higher density, such as, for example, sand,ceramic, bauxite, or resin coated proppant. The density differentialbetween the first proppant stage, or pad fluid, and second proppantstage is preferably at least 0.2 g/cc.

The method of incorporating two or more proppant stages under thedefined conditions, or using two or more mixed proppants in a singleproppant stage, having a ULW proppant provides significant benefitsrelative to treatments with conventional high-density proppants. Inaddition, the method provides significant benefits as compared to priorart methods. Such benefits include a reduction in costs and thepotential for significantly improved effective propped fracture length.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a 2D depiction of a fracture, after closure of the fracture,initiated with a fluid pad not containing a ULW proppant, the fracturebeing successively treated with a second proppant stage.

FIG. 2 is a 2D depiction of a fracture, after closure of the fracture,initiated with a fluid pad containing a ULW proppant, the fracture beingsuccessively treated with a second proppant stage.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The method of fracturing a hydrocarbon-bearing subterranean formation,as defined by the invention, provides greater effective propped fracturelength than seen with conventional fracturing techniques. Effectivepropped fracture lengths may be increased by as much as 100%. Suchgreater effective propped fracture length translates to improvedstimulation efficiency, well productivity and reservoir drainage.

While not intending to be bound by any theory, it is believed that theenhanced effective length of the propped fracture is attributable to thereduced cross-sectional flow area existing above the settled bank. Wherethe first proppant stage is used to propagate the fracture, it isbelieved that the reduced cross-sectional flow area exists above thesettled bank generated by this first proppant stage. Assuming constantpumping rates at the wellbore, the reduced cross-sectional area“artificially” increases the velocity of the second or successiveproppant stages through that section of the fracture, leading toimproved transport and deeper placement of the second or successiveproppant stages into the fracture than would be achieved within thecreated fracture in the absence of the proppant bank.

In a preferred embodiment, the method of the invention consists offracturing by introducing into the formation the use of multipleproppant stages wherein at least one of the proppant stages contains aULW density proppant. Alternatively, the method consists of using asingle proppant stage containing at least two proppants, wherein atleast one of the proppant stages contains a ULW density proppant. Asdefined herein, a ULW proppant is one which has a density less than orequal to 2.45 g/cc.

The formation may first be propagated by introducing into the formationa proppant stage at a pressure sufficient to propagate the fracture.This proppant stage, which initiates the fracture, typically contains aconventional high-density proppant, though it may contain, in additionto or in lieu of the conventional high-density proppant, a ULW proppant.

The “first proppant stage” of the invention may refer to either theproppant stage introduced into the formation to propagate the fractureor a proppant stage introduced into the formation after propagation hasoccurred. Thus, the term “first proppant stage” is not to be construedas encompassing only the first proppant stage introduced to the fractureor formation. It is meant only to refer to a proppant stage whichprecedes a “second proppant stage.”

The “first proppant stage” may contain a mixture of proppants, at leastone of which is a ULW proppant. In a preferred mode, the first proppantstage contains at least two proppants. In a more preferred mode, thedensity differential of the two proppants in this mixture is greaterthan or equal to 0.2 g/cc. Where more than two proppants are present inthe mixture, the density differential between at least two of theproppants in the mixture is greater than or equal to 0.2 g/cc. Inanother preferred mode, at least two proppants of the first proppantstage are ULW proppants. Depending on the operator, where the firstproppant stage contains a mixture of such proppants, it may be desirousto introduce a second proppant stage into the formation after theintroduction of the first proppant stage.

If the first proppant stage contains either a single proppant (eitherconventional high-density or ULW proppant) or a mixture of proppants,none of which are a ULW proppant, it is typically necessary to introducea subsequent proppant stage into the formation. (As used herein, theterm “conventional high-density proppant” refers to a proppant having adensity greater than 2.45 g/cc.) This successive proppant stage isreferred to herein as the “second proppant stage”. It may be introducedinto the formation immediately after the first proppant stage.Alternatively, at least one additional proppant stage may be introducedinto the formation after the first proppant stage but before the secondproppant stage.

Where a second proppant stage is employed, it is preferred that at leastone of the following conditions should further prevail:

(i.) the first proppant stage and/or second proppant stage contains amixture of proppants, at least one of which is a ULW proppant and,preferably wherein the density differential between at least two of theproppants in the mixture is greater than or equal to 0.2 g/cc;

(ii.) the first proppant stage and/or the second proppant stage containsa ULW proppant and the density differential between the first proppantstage and the second proppant stage is greater than or equal to 0.2g/cc, preferably greater than or equal to 0.50 g/cc, most preferablygreater than or equal to 0.80 g/cc. Preferably, the density of thesecond proppant stage is less than the density of the first proppantstage. For instance, the density of the proppant of the first proppantstage may be around 2.65 and the density of the proppant of the secondproppant stage may be 1.90;

(iii.) both the first proppant stage and the second proppant stagecontain ULW proppants;

(iv.) the proppant of the first proppant stage and/or the secondproppant stage contain a ULW proppant and the rate of injection of thesecond proppant stage into the fracture is different from the rate ofinjection of the first proppant stage. Typically, the rate of injectionof the second proppant stage is lower than the rate of injection of thefirst proppant stage. Typically the rate of injection of each of theproppant stages is greater than or equal to 5 barrels per minute. Therate of injection of any given proppant stage may be as high as 250barrels/minute; or

(v.) the proppant of the first proppant stage and/or second proppantstage contain a ULW proppant and the particle size of the secondproppant stage is different from the particle size of the first proppantstage; typically, the particle size of the proppant of the secondproppant stage is greater than the particle size of the proppant of thefirst proppant stage, especially where the second proppant stage isdirected more towards the wellbore and smaller than the particle size ofthe proppant of the first proppant stage especially where the secondproppant stage is directed further into the fracture. Typically, theparticle size of the proppant with the proppant system used in theinvention is from about 8/12 US mesh to about 100 US mesh. Mosttypically, the particle size of the proppant with the proppant systemused in the invention is from about 12/20 US mesh to about 40/70 USmesh.

Successive proppant stages may be injected into the fracture afterinjection of the second proppant stage. Thus, the invention may consistof multiple proppant introductions provided at least one of thefollowing conditions prevail:

(i.) the differential in density between the ultimate (successive)proppant stage and the penultimate proppant stage is greater than orequal to 0.2 g/cc;

(ii.) the rate of injection of the ultimate proppant stage into thefracture is different from the rate of injection of the penultimateproppant stage; typically, the rate of injection of the ultimateproppant stage into the fracture is lower than the rate of injection ofthe penultimate proppant stage into the fracture; or

(iii.) the particle size of the ultimate proppant stage is differentfrom the particle size of the penultimate proppant stage.

The limitation to the number of stages employed is principally basedupon practicality from an operational perspective.

The effective propped length of the fracture after injection of theultimate proppant stage is preferably greater than the effective proppedlength of the penultimate proppant stage.

In a preferred embodiment, the first proppant stage comprises a mixtureof a first proppant and a second proppant, wherein the first proppant isa conventional high-density proppant, such as sand, ceramic, sinteredbauxite or resin coated proppant, and the second proppant is a ULWproppant having a density less than or equal to 2.45 g/cc.

In another preferred embodiment, the process of the invention requiresat least two proppant stages wherein the density differential betweenthe first proppant stage and the second proppant stage is at least 0.2g/cc. While the second proppant stage in such instances will require atleast one ULW, the first proppant stage may contain either aconventional high-density proppant or a ULW.

Thus, for instance, the first proppant stage may be a banking fluid usedto cause the initial propagation of the formation, allowing it to form aproppant bank. The banking fluid may contain a conventional high-densityproppant. A subsequent second proppant stage may include a ULW proppant,exhibiting a particle density substantially lower than the density ofthe conventional high-density proppant. For instance, the proppant ofthe subsequent proppant stage may have a density ranging between fromabout 1.25 g/cc to about 1.75 g/cc.

Proppant stages containing ULW proppants are less subject to settlingthan conventional proppant stages and are more easily transported toprovide greater effective propped fracture length.

In addition, the method of the invention offers a reduction in costs andthe potential for significantly improved effective propped fracturelength.

As an example of the process of the invention, a hydrocarbon-bearingsubterranean formation may be hydraulically fractured by firstintroducing into the formation a first proppant stage. This firstproppant stage may be a first fracturing fluid and may be introduced ata pressure sufficient to initiate a fracture. Alternatively, this firstproppant stage may be introduced into the fracture after the fracturehas been propagated. This initial (first) proppant stage may then befollowed by fracturing the subterranean formation with a subsequentfracturing fluid, or second proppant stage. The number of successiveproppant stages introduced into the fracture is determined by thepreferences of the operator.

In a preferred embodiment of the invention, the fracturing fluid or “padfluid” used to initiate the fracture may contain at least one ULWproppant. Fracture conductivity is greatly improved by the incorporationof small amounts of a ULW proppant in the pad fluid. The effectivepropped length of a fracture pumped with a ULW proppant-containing padstage is greater than the effective propped fracture length of afracture pumped with a substantially similar pad fluid not containing aULW proppant. By “substantially similar pad fluid” is principally meanta pad fluid identical to the ULW proppant-containing pad stage but notcontaining the ULW proppant.

Typically, the amount of ULW proppant in the pad fluid is between fromabout 0.12 to about 24, preferably between from about 0.6 to about 9.0,weight percent based on the total weight percent of the fracturingfluid. The proppant in the second proppant stage (following the padstage) contains either a ULW proppant or a conventional high densityproppant. The concentration of the ULW or conventional high densityproppant in the second proppant stage is typically greater than or equalto the concentration of ULW proppant in the pad fluid. Preferably, thedensity differential between the proppant of the first proppant stage(pad fluid) and the second proppant stage is at least 0.2 g/cc.

The fracturing fluid may include any conventional fluid treatment suchas crosslinked organoborate gels, guar or cellulosic based slickwaters,brines, linear gels and foams. The fracturing fluid may further containa fine particulate, such as sand, for fluid loss control, etc.

In a preferred embodiment, the initial (first) fracturing fluid maycontain a breaker. Further preferable, however, is the use of slickfluids, such as those exhibiting reduced water friction, as the initialstage which do not require a breaking fluid. Other proppant stages mayoptionally contain a breaker. The breaker can be any conventionallyemployed in the art to reduce the viscosity of the fracturing fluidincluding, but not being restricted to, thermostable polymers. Dependingon the application, a breaker of predictable performance may beincorporated into the initial fracturing fluid or any of the proppantstages referred to herein for downhole activation.

A “spearhead” fluid may further precede the introduction of thefracturing or pad fluid to clean-up undesired products, such as ferroussulfide and/or ferric oxide. Such fluids are typically introduced intothe reservoir at fracturing rates and pressures which initiate thefracture in the formation and contain components known in the art.

The initial fracturing fluid, as well as any of the proppant stagesreferred to herein, may also contain other conventional additives commonto the well service industry such as surfactants, biocides, gellingagents, cross-linking agents, curable resins, hardening agents,solvents, foaming agents, demulsifiers, buffers, clay stabilizers,acids, or mixtures thereof. In the practice of the invention, thefracturing fluid may be any carrier fluid suitable for transporting amixture of proppant into a formation fracture in a subterranean well.Such fluids include, but are not limited to, carrier fluids comprisingsalt water, fresh water, liquid hydrocarbons, and/or nitrogen or othergases.

The initial fracturing fluid of the invention is pumped at a ratesufficient to initiate and propagate a fracture in the formation and toplace the proppant into the fracture and form a bank. During the actualpumping the pH may be adjusted by the addition of a buffer, followed bythe addition of the enzyme breaker, crosslinking agent, proppant oradditional proppant and other additives if required. After deposition,the proppant material serves to hold the fracture open, therebyenhancing the ability of fluids to migrate from the formation to thewellbore through the fracture.

Typically, viscous gels or foams are employed as the fracturing fluid inorder to provide a medium that will adequately suspend and transport thesolid proppant, as well as to impair loss of fracture fluid to theformation during treatment (commonly referred to as “filterability” or“fluid loss”). As such, viscosity of the fracturing fluid may affectfracture geometry because fluid loss affects the efficiency of atreatment. For example, when the rate of fluid loss to the formationequals or exceeds the rate of injection or introduction of fluid into afracture, the fracture stops growing. Conversely, when the rate of fluidloss is less than the injection or introduction rate, taken togetherwith other factors, a fracture continues to propagate. Excessive fluidloss thus results in fractures that are smaller and shorter thandesired.

In one embodiment, the proppants disclosed herein may be introduced orpumped into a well as, for example, a saturated sodium chloride solutioncarrier fluid or a carrier fluid that is any other completion orworkover brine having, for example, a specific gravity of from about 1to about 1.5, alternatively from about 1.2 to about 1.5, furtheralternatively about 1.2, at temperatures up to about 150° F. andpressures up to about 1500 psi. However, these ranges of temperature andclosure stress are exemplary only, it being understood that thematerials may be employed as proppant materials at temperatures greaterthan about 150° F. and/or at closure stresses greater than about 1500psi. It also being understood that core and/or layer materials may beselected by those of skill in the art to meet and withstand anticipateddownhole conditions of a given application.

Preferably, the successive proppant stages (those proppant stagessubsequent to the initial fracture proppant stage) include carriersystems that are gelled, non-gelled, or that have a reduced or lightergelling requirement as compared to carrier fluids employed withconventional fracture treatment methods.

Conventional high-density proppants may be used in the first proppantstage, especially where the first proppant stage is used as the initialfracturing fluid, as well as in successive proppant stages (after theinitial fracturing stage), may be any conventional proppant in the art.Such proppants include, for instance, quartz, glass, aluminum pellets,silica (sand) (such as Ottawa, Brady or Colorado Sands), syntheticorganic particles such as nylon pellets, ceramics (includingaluminosilicates such as “CARBOLITE,” “NAPLITE” or “ECONOPROP”),sintered bauxite, and mixtures thereof. In addition, protective and/orhardening coatings, such as resins to modify or customize the density ofa selected base proppant, e.g., ground walnut hulls, etc., resin-coatedsand (such as “ACME BORDEN PR 6000” or “SANTROL TEMPERED HS”),resin-coated ceramic particles and resin-coated sintered bauxite may beemployed.

Preferred high-density proppants are sand, ceramic, sintered bauxite andresin coated proppant. Such proppants typically exhibit a high density,for instance greater than 2.65 g/cc. Typically, sand or syntheticfracture proppants are used. Such proppants are normally used inconcentrations between about 1 to 18 pounds per gallon of fracturingfluid composition, but higher or lower concentrations can be used asrequired.

The ULW proppant is defined as having a density less than or equal to2.45 g/cc. Generally, the density of the ULW proppant is less than orequal to 2.25, more preferably less than or equal to 2.0, even morepreferably less than or equal to 1.75, most preferably less than orequal to 1.25 g/cc. Such proppants are less subject to settling and canbe more easily transported to provide greater effective propped fracturelength. Greater effective propped fracture length translates to improvedstimulation efficiency, well productivity and, reservoir drainage.

In a preferred embodiment, the second proppant stage contains a proppanthaving a density less than the density of the proppant in the firstproppant stage. In a preferred embodiment, successive third proppantstages contain a proppant having a density less than the density of theproppant of the second proppant stage. Preferably, the densitydifferential between the proppant of the third proppant stage and theproppant of the second stage is greater than or equal to 0.2 g/cc. Thus,in a preferred embodiment of the invention, two or more proppants arepumped in successive stages; each successive stage utilizing a proppantof lower density.

Such ULW proppants may be represented by relatively lightweight orsubstantially neutrally buoyant materials. One of the benefits of usingsuch materials is that the requirements for the mixing equipment areminimized. For instance, when the carrier fluid is a brine, the onlyrequirements on the mixing equipment is that it be capable of (a) mixingthe brine (dissolving soluble salts), and (b) homogeneously dispersingin the substantially neutrally buoyant particulate material.

By “relatively lightweight” it is meant that the material has a densitythat is substantially less than a conventional proppant employed inhydraulic fracturing operations, e.g., sand or having a density similarto these materials. By “substantially neutrally buoyant”, it is meantthat a material having a density sufficiently close to the density of anungelled or weakly gelled carrier fluid (e.g., ungelled or weakly gelledcompletion brine, other aqueous-based fluid, or other suitable fluid) toallow pumping and satisfactory placement of the proppant using theselected carrier fluid. For example, urethane resin-coated ground walnuthulls having a specific gravity of from about 1.25 to about 1.35grams/cubic centimeter may be employed as a substantially neutrallybuoyant proppant in completion brine having a density of about 1.2. Itwill be understood that these values are exemplary only. As used herein,a “weakly gelled” carrier fluid is a carrier fluid having minimumsufficient polymer, viscosifier or friction reducer to achieve frictionreduction when pumped down hole (e.g., when pumped down tubing, workstring, casing, coiled tubing, drill pipe, etc.), and/or may becharacterized as having a polymer or viscosifier concentration of fromgreater than 0 pounds of polymer per thousand gallons of base fluid toabout 10 pounds of polymer per thousand gallons of base fluid, and/or ashaving a viscosity of from about 1 to about 10 centipoises. An ungelledcarrier fluid may be characterized as containing about 0 pounds perthousand gallons of polymer per thousand gallons of base fluid. Suchrelatively lightweight and/or substantially neutrally buoyant materialsare disclosed in U.S. Pat. No. 6,364,018, herein incorporated byreference. Exemplary of such relatively lightweight and/or substantiallyneutrally buoyant fracture proppant material is a ground or crushedwalnut shell material that is coated with a resin to substantiallyprotect and water proof the shell. Such a material may have a specificgravity of from about 1.25 to about 1.35, and a bulk density of about0.67.

Examples of types of materials suitable for use as relativelylightweight and/or substantially neutrally buoyant proppant materialsinclude, but are not limited to, ground or crushed shells of nuts suchas walnut, pecan, almond, ivory nut, brazil nut, etc.; ground or crushedseed shells (including fruit pits) of seeds of fruits such as plum,peach, cherry, apricot, etc.; ground or crushed seed shells of otherplants such as maize (e.g. corn cobs or corn kernels), etc., crushedfruit pits or processed wood materials such as those derived from woodssuch as oak, hickory, walnut, poplar, mahogany, etc. including suchwoods that have been processed by grinding, chipping, or other form ofparticleization. Additional information on such materials and methodsfor use thereof may be found in U.S. Pat. No. 6,330,916 and in U.S. Pat.No. 6,059,034, herein incorporated by reference.

Those of skill in the art will understand that selection of suitableproppant will depend, in part, on the density of the carrier fluid andon whether it is desired that the selected proppant particle berelatively lightweight or substantially neutrally buoyant in theselected carrier fluid, and/or whether or not it is desired that thecarrier fluid be non-gelled or non-viscosified.

The ULW proppants employed in the invention, including the relativelylightweight and/or substantially non-buoyant proppants, may be chipped,ground, crushed, or otherwise processed to produce particulate materialhaving any particle size or particle shape suitable for use in themethods disclosed herein. Typically, the particle sizes of the proppantsemployed in the invention range from about 4 mesh to about 100 mesh,alternatively from about 8 mesh to about 60 mesh, alternatively fromabout 12 mesh to about 50 mesh, alternatively from about 16 mesh toabout 40 mesh, and alternatively about 20 to 40 mesh. In one exemplarycase, the proppant may ground walnut shells having a particle size ofabout 12/20 US mesh size in the first proppant stage and 20/40 US meshsize in the second proppant stage.

In a preferred mode, the second proppant stage is introduced into theformation immediately after the first proppant stage and the thirdproppant stages is introduced into the formation immediately after thesecond proppant stage without any intervening proppant stages.

Further, in a preferred mode, where the injection rate of a successiveproppant stage is identical to the injection rate of the proppant stageintroduced into the fracture immediately before the successive proppantstage or where the density of the proppant of the successive proppantstage is identical or less than the density of the proppant of theproppant stage introduced into the fracture immediately before thesuccessive proppant stage, the particle size of the proppant of thesuccessive proppant stage is different from the particle size of theproppant of the proppant stage introduced into the fracture immediatelybefore the successive proppant stage.

Fracture proppant sizes may be any size suitable for use in a fracturingtreatment of a subterranean formation. It is believed that the optimalsize of the proppant material may be dependent, among other things, onthe size of the fracture, on in situ closure stress. As an example ofthe variance of the particle size in the invention, the particle size ofthe proppant of the first (initial) proppant stage may be 40 mesh whilethe particle size of the proppant of the second proppant size may be 30mesh.

It is possible further that the particle size of the proppant betweensuccessive fractures may differ due to the coatings on the proppants.For instance, a proppant of a second proppant stage may be selected fromat least one of ground or crushed nut shells, ground or crushed seedshells, ground or crushed fruit pits, processed wood, or a mixturethereof. A proppant of a first proppant stage may additionally includeat least a portion of the individual particles of the particulatematerial above as core component which is at least partially surroundedby at least one layer component of the second proppant, the firstproppant including a protective or hardening coating. Under suchcircumstances, if the core of the first proppant is identical to thecore of the second proppant, the first proppant would have a greaterparticle size.

The potential for significantly improved effective propped fracturelength is evidenced by use of the method of the invention. This may bedue to the reduced cross-sectional flow area existing above the settledbank generated by the first proppant pumped. Assuming constant pumpingrates at the wellbore, the reduced cross-sectional area ‘artificially’increases the successive reduced density proppant slurry velocities through that section of the fracture, leading to improved transport anddeeper placement of those slurry stages into the fracture than would beachieved within the created fracture in the absence of the proppantbank.

Under some circumstances deformable particles having a sizesubstantially equivalent or larger than a selected fracture proppantsize may be employed. Such deformable particles are discussed above. Forexample, a deformable particulate material having a larger size than thefracture proppant material may be desirable at a closure stress of about1000 psi or less, while a deformable particulate material equal in sizeto the fracture proppant material may be desirable at a closure stressof about 5000 psi or greater. However, it will be understood withbenefit of this disclosure that these are just optional guidelines. Inone embodiment, a deformable particle is selected to be at least as bigas the smallest size of fracture proppant being used, and may beequivalent to the largest fracture proppant grain sizes. In either case,all things being equal, it is believed that larger fracture proppant anddeformable particulate material is generally advantageous, but notnecessary. Although deformable particulate material smaller than thefractured proppant may be employed, in some cases it may tend to becomewedged or lodged in the fracture pack interstitial spaces. In oneembodiment, deformable particles used in the disclosed method may have abeaded shape and a size of from about 4 mesh to about 100 mesh,alternatively from about 8 mesh to about 60 mesh, alternatively fromabout 12 mesh to about 50 mesh, alternatively from about 16 mesh toabout 40 mesh, and alternatively about 20/40 mesh. Thus, in oneembodiment, deformable particles may range in size from about 1 or 2 mmto about 0.1 mm; alternatively their size will be from about 0.2 mm toabout 0.8 mm, alternatively from about 0.4 mm to about 0.6 mm, andalternatively about 0.6 mm. However, sizes greater than about 2 mm andless than about 0.1 mm are possible as well.

Deformable particles may be mixed and pumped with fracture proppantmaterial throughout or during any portion of a hydraulic fracturingtreatment in the practice of the disclosed method. However, in oneembodiment when deformable particulate material is mixed with only aportion of a fracture proppant material pumped into a formation, it maybe mixed with proppant during the latter stages of the treatment inorder to dispose the deformable particulate material in the fracturepack at or near the point where the wellbore penetrates a subterraneanformation.

Deformable particles having any density suitable for fracturing asubterranean formation may be employed in the practice of the disclosedmethod. In one embodiment specific gravity of deformable particulatematerial may range from about 0.3 to about 12, alternatively from about0.4 to about 12, and further alternatively from about 0.5 to about 12.In another embodiment, the specific gravity of a deformable particulatematerial is from about 0.3 to about 3.5, alternatively from 0.4 to about3.5, alternatively from about 0.5 to about 3.5, alternatively from about0.6 to about 3.5, and even alternatively from about 0.8 to about 3.5.Alternatively a deformable particulate material having a specificgravity of from about 1.0 to about 1.8 is employed, and alternatively adeformable particle having a specific gravity of about 1.0 to about 1.1is employed. In another specific embodiment, a particular divinylbenzenecrosslinked polystyrene particle may have a bulk density of from about0.4 to about 0.65, and alternatively of about 0.6. In another specificexemplary embodiment, a particular divinylbenzene crosslinkedpolystyrene particle may have a specific gravity of about 1.055.However, other specific gravities are possible. Advantageously, in oneembodiment when deformable particles having a density less than that ofa selected fracture proppant material are employed, reduced treatingpressures and concentration levels of potentially formation-damaginggelled or viscous fluids may be employed. This may allow higher treatingrates and/or result in higher formation productivity.

Lastly, in a preferred mode, the second or ultimate proppant stage isinjected into the fracture at a rate different from the injection rateof the first or penultimate proppant stage. Preferably, the rate ofinjection of the ultimate proppant stage is less than the rate ofinjection of the penultimate proppant stage. Typically, the rate ofinjection of a proppant stage into the formation or fracture inaccordance with the invention is from about 5 barrels per minute to ashigh as 270 barrels per minute. Generally, the rate of injection is nogreater than about 150 barrels per minute.

Additionally, the same arguments for this approach would apply whenusing more viscous fluids such as linear or crosslinked fluids,particularly when considering applications in more rigorous downholeenvironments (i.e., higher temperatures).

Further, subsequent to creating the fracture, it may be advantageous toreverse the process and fracture back to the wellbore filling thewellbore. This can be achieved in sequential steps such that at leastone of the following conditions prevails after each successive stage:

(1) the density of the successive (ultimate) stage being injected intothe wellbore is generally less than the density of the stage introducedto the wellbore just prior (penultimate) to the successive stage;

(2) the rate of injection of the ultimate stage being injected into thefracture is less than the rate of injection of the penultimate stage; or

(3) the particle size of the proppant of the ultimate stage beinginjected into the fracture is different than the particle size of theproppant of the penultimate stage.

The following examples will illustrate the practice of the presentinvention in its preferred embodiments. Other embodiments within thescope of the claims herein will be apparent to one skilled in the artfrom consideration of the specification and practice of the invention asdisclosed herein. It is intended that the specification, together withthe examples, be considered exemplary only, with the scope and spirit ofthe invention being indicated by the claims that follow.

EXAMPLES Example 1 (Comparative)

This Example demonstrates the settling rates for Ottawa sand and WalnutHull ULW.

ULW 1.75 is porous ceramic material from Carbo Ceramics, Inc. treatedwith 2% by weight of particle epoxy inner coating/penetrating material(epoxy is reaction product of epichlorohydrin and bis-phenol A) and with2% by weight of particle phenol formaldehyde resin outer coatingmaterial. It can be characterized as a porous ceramic particle with theroundness and sphericity common to ceramic proppants. The porosityaverages 50%, yielding a bulk density of 1.10 to 1.15 g/cm³.Median-sized 20/40 particles of the ULW-1.75 and Ottawa sand were used.The 20/40 Ottawa sand has an average bulk density of 1.62 g/cm with aspecific gravity of 2.65. The ULW-1.75 has a bulk density of 1.05 to1.10.

Static particle settling evaluations were conducted in fresh water todetermine the differences in settling rate between the conventionalproppant and the ULW particles. Median sized 20/40 particles of eachproppant were used for the evaluations. Stokes Law calculations givingthe fall velocity in ft/minute are presented in Table 1 and werecalculated as:V=1.15×10³(d _(prop) ²/μ_(fluid))(Sp.Gr. _(prop) −Sp.Gr. _(fluid))where velocity is in ft/min., diameter d is the average particlediameter and, μ is fluid viscosity in cps.

TABLE 1 Static Settling Rates for Proppants as Derived by Stoke's Law20/40 Proppant Sp. Gr. Settling Velocity ft/minute Ottawa sand 2.65 16.6ULW-1.75 1.75 11.2

Large-scale slot flow tests were conducted to characterize the dynamicsettling rates of the ultra-lightweight proppant. Proppant transportcharacteristics were studied at ambient temperature through a glassslot. The transparent slot is a 22-inch high, 16-ft long and 0.5-inchwide parallel plate device. One thousand gallons of test fluid wasprepared and the fluid rheology was measured using a standard Fann 35viscometer. Fluid was then transferred to a 200-gallon capacity ribbonblender and pumped through the test loop to fill the transparent slotmodel. Once the slot was filled with the test fluid, proppant was addedto the blender to prepare a slurry of the desired concentration. Theslickwater fluid used in the test exhibited an average viscosity of 5 to7 cps throughout the series of tests.

The shear rate in the slot is given by the equation:

$\gamma = {\left\lbrack \sec^{- 1} \right\rbrack = \frac{1.925{q\mspace{14mu}\lbrack{gpm}\rbrack}}{\left( {w\left\lbrack {{in}.} \right\rbrack} \right)^{2}\left( {H\lbrack{ft}\rbrack} \right)}}$where q is the rate in gallons per minute, w is width in inches and H isheight in feet. Fluid velocity through this slot model is given by:

${v\left\lbrack {m\text{/}\sec} \right\rbrack} = \frac{0.00815{q\mspace{14mu}\lbrack{gpm}\rbrack}}{\left( {w\left\lbrack {{in}.} \right\rbrack} \right)\left( {H\lbrack{ft}\rbrack} \right)}$

The proppant transport behavior of each test slurry was observed throughthe slot at various flow rates. During these tests, the proppantdistribution was continually recorded with video cameras as well asmanually by observation. All bed height measurements for this work weretaken close to the discharge end of the slot flow cell.

Ottawa sand slurried in slickwater was observed to begin settling uponentrance to the slot even at the maximum fluid pump rate. Within 12minutes at 90 gpm (378 sec−1 shear rate), the bed height was 15 inches,68% of the total height of the 22 in slot. Table 2 below shows theresults in tabular form. Only at shear rates in excess of 1000 sec−1 wasthe dynamic Ottawa Sand proppant fall rate mitigated in the slickwatertest fluid. As flow rates were lowered to 30 gpm, the Ottawa proppantbed reached its maximum bed height of 19.5 inches or 91.25% of the slotheight. Above the proppant bed, the shear rate reached 1,414 sec−1, atwhich point additional settling did not occur. As the rate increasedfrom 30 to 40 gpm (1,919 sec−1), the bed height was actually reduced.

TABLE 2 Time, Fluid Rate Prop Bed Slot Shear Above bed, minute GpmHeight (ft) Sec-1 sec-1 0 90 0 378 378 1 90 0.25 383 443 12 90 1.25 3811201 14 60 1.27 252 825 18 60 1.38 252 825 19 40 1.39 168 677 28 40 1.54170 1076 30 30 1.58 116 858 42 30 1.67 171 1414 43 40 1.67 171 1919 4540 1.52 169 1070

The ULW-1.75 test was initiated at 90 gpm. ULW-1.75 was observed to besubject to some settling at 90 gpm, with the bed height growing to 4inches. The fluid rate was lowered to 80 gpm and bed height grew to 6inches. As the rates were reduced incrementally down to 30 gpm, theULW-1.75 bed was observed to grow with reduced rate to 12 inches. Therate was lowered further to 5 gpm and the bed height grew to 19 inchesor 86% of the total slot height. As observed in previous tests, as therate is increased incrementally, bed height decreases due to erosion andfluidization of the bed. The ULW-1.75 results are presented in Table 3.

TABLE 3 Time, Fluid Rate Prop Bed Slot Shear Above bed, minute GpmHeight Sec-1 sec-1 0 90 0.0 378 378 7 90 0.33 378 463 8 80 0.38 337 42311 80 0.54 337 478 12 70 0.58 295 432 15 60 0.71 252 412 17 60 0.79 252445 18 50 0.83 210 386 20 50.4 0.92 212 425 22 39 0.96 164 345 23 30 1126 278 28 31 1.29 130 443 29 20 1.33 81 299 33 8 1.44 34 159 34 5.11.46 21 106 35 20 1.54 84 534 37 20.5 1.58 86 640 38 40.4 1.52 170 100640 50.6 1.46 213 1048 45 60.2 1.33 253 933

Both of the tested materials settle progressively more as the velocitydecreases. Due to the decreased density, the ULW is more easily placedback in flow as the rate is increased. The reduced density materialsrequire less shear increase to fluidize the proppant bed. Ottawa sandwas observed to require in excess of 1,500 sec−1 to transport theproppant in slickwater and almost 2,000 sec−1 of shear to begin tofluidize the proppant bed. The ULW-1.75 transporting at shear rates of500 sec−1 and fluid shear rates of 800 sec−1 were needed to fluidize theproppant bed.

Example 2

This Example illustrates use of the combination of both sand and walnuthull ULW proppants.

One hundred pounds of sand and 50 pounds of walnut hull ULW proppantwere blended together in a ribbon blender and circulated throughout thesystem. The blend displayed behavior almost identical to theirindividual tests, respectively. The sand settled even at very high flowrates, throughout the length of the slot as in the earlier test.

Because sand built bed height continuously throughout the test, the ULWproppant stayed suspended. Lateral velocity was increased by the sandbed, so very little ULW proppant was entrained in the sand bed. This isattributable to the fact that the sand bed height artificially increasedlateral velocities in the slot to levels that maintained the ULWproppant in suspension for the most part. Most of the sand settled outin the slot before any ULW proppant began to settle. Rates had to bedropped down to below 10 gpm in order to initiate larger scale settlingof the ULW material and by that time, there was little sand left tosettle.

The process presents a suitable means to improve penetration of proppantinto a productive horizon. Both proppants behave independently from eachother, yet the settling of the heavier proppant improves the ability ofthe lighter proppant to move deeper in the fracture by partiallyoccluding the open flow space. It is reasonable to assume that thebehavior will extend to more than two proppants in a given slurry and assuch may offer additional advantages in fracture placement andpropagation. This offers advantages for slickwater fracturing operationsas they are currently conducted.

Example 3

This Example demonstrates the improvement in fracture conductivity byuse of a ULW proppant as a component in a pad fluid.

A fracture was simulated using the Mfrac three-dimensional hydraulicfracturing simulator of Meyer & Associates, Inc. using a simple 3-layerisotropic homogeneous 0.1 mD permeability gas reservoir model, 40 acrespacing. The fracture was designed to be placed into the zone at atheoretical depth of 9800 feet and the model was run in full 3-D mode.The fracturing fluid was a crosslinked organoborate. The pad fluid wasinjected into the model at a rate of 50 barrels per minute (bpm). Thefracturing fluid of Example 3A contained no ULW proppant. In Example 3B,a very small amount (0.5 pounds per gallon) of LiteProp™ 125 lightweightproppant, a product of BJ Services Company, was added to the fracturingfluid. The second and subsequent stages employed sand as proppantwherein the sand concentration was approximately 8 ppg. Since the Mfracmodel does not make calculations for a partial monolayer, theconductivity of the proppant was artificially increased at aconcentration of 0.5 lbs/sq. ft. Table 4 shows the pump scheduleutilized for Example 3A and Table 5 shows the pump schedule for Example3B.

TABLE 4 Stage Stage Liquid Prop Damage No. Slurry Rate Volume Stage TimeStage Type Fluid Type Prop Type Prop Conc. Factor (−) (bpm) (U.S. gal)(min) (−) (−) (−) (lbm/gal) (−) 1 50 20000 9.5238 Pad B095 0000 0 0 2 5010000 5.1929 Prop B095 0001 2 0 3 50 10000 5.6239 Prop B095 0001 4 0 450 10000 6.0548 Prop B095 0001 6 0 5 50 10000 6.4858 Prop B095 0001 8 06 50 9600 4.5714 Flush SG20 0000 0 0 Wellbore Fluid Type: 2% KClB095-Spectra Frac HT 3500 w/4.0 gpt BF-7L, 2.0 gpt XLW-56 crosslinker,products of BJ Services Company, Fluid Type: SG20-2% KCl guar slickwater20# Proppant Type: 0000-No Prop, Slug Proppant Type: 0001-20/40 JordanSand

TABLE 5 Stage Stage Liquid Prop Damage No. Slurry Rate Volume Stage TimeStage Type Fluid Type Prop Type Prop Conc. Factor (−) (bpm) (U.S. gal)(min) (−) (−) (−) (lbm/gal) (−) 1 50 20000 9.9803 Pad B095 SG19 0.5 0 250 10000 5.1929 Prop B095 0001 2 0 3 50 10000 5.6239 Prop B095 0001 4 04 50 10000 6.0548 Prop B095 0001 6 0 5 50 10000 6.4858 Prop B095 0001 80 6 50 9600 4.5714 Flush SG20 0000 0 0 Wellbore Fluid Type: 2% KClB095-Spectra Frac HT 3500 w/4.0 gpt BF-7L, 2.0 gpt XLW-56 crosslinker,products of BJ Services Company, Fluid Type: SG20-2% KCl guar slickwater20# Proppant Type: SG19-ULW 125 partial monolayer Proppant ProppantType: 0001-20/40 Jordan Sand Proppant Type: 0000-No Prop, SlugFracture conductivity between the proppant-packed fracture and that ofthe native reservoir, mathematically defined as:(proppant pack permeability×fracture width)/(formationpermeability×propped fracture half length)is illustrated in the conductivity profiles of FIGS. 1 and 2 afterclosure of the fracture. FIG. 1 is a 2D depiction of the fracture ofinjection of the fracturing fluid of Example 3A. FIG. 2 contrastsinjection of the fracturing fluid of Example 3B. In both figures, the“created fracture area,” represented as 10, is the area of the reservoirtraversed by the propagating fracturing fluid pad. The “propped fracturearea”, 20, is contributory to well stimulation, and represents the areaof the reservoir “propped open” to provide improved fractureconductivity. The created but unpropped area 30, “heal” upon fractureclosure and, thus, is not considered to be stimulated.

As set forth in FIGS. 1 and 2, the propped fracture length is increasedfrom approximately 320 ft to approximately 460 feet by the addition ofthe ULW proppant and all of the proppant ends in the pay zone, definedby the area within 40 and 50. The Figures demonstrate greatly improvedfracture conductivity by the incorporation of a ULW proppant into apreviously non-proppant laden pad fluid. This results in an enhancedfracture length which leads to enhanced well productivity, produciblewell reserves and ultimate expected recovery. Use of the ULW proppantsavoid failure due to settling and bridging of the particles.

The foregoing disclosure and description of the invention isillustrative and explanatory thereof, and various changes in the size,shape, and materials, as well as in the details of illustrativeconstruction and assembly, may be made without departing from the spiritof the invention.

1. A method of hydraulically fracturing a hydrocarbon-bearingsubterranean formation which comprises: pumping a first proppant stageeither into a propagated fracture or into the formation at a pressuresufficient to fracture the formation; and pumping a second proppantstage into the fracture wherein at least one of the following conditionsprevails: (i.) the density differential between the first proppant stageand the second proppant stage is greater than or equal to 0.2 g/cc andeither the first proppant stage and/or the second proppant stagecontains an ultra lightweight (ULW) proppant; (ii.) the proppant of thefirst proppant stage and/or the second proppant stage contains a ULWproppant and the rate of injection of the second proppant stage into thefracture is different from the rate of injection of the first proppantstage; or (iii.) the proppant of the first proppant stage and/or thesecond proppant stage contains a ULW proppant and the particle size ofthe proppant of the second proppant stage is different from the particlesize of the proppant of the first proppant stage.
 2. The method of claim1, wherein the first proppant stage and/or the second proppant stagecontains a first proppant and a second proppant, wherein both the firstproppant and second proppant are a ULW proppant.
 3. The method of claim1, wherein the first proppant stage is a pad fluid and contains a ULWproppant.
 4. The method of claim 3, wherein the effective propped lengthof the fracture after pumping of the first proppant stage is greaterthan the effective propped fracture length of a fracture pumped with asubstantially similar pad fluid which does not contain a ULW proppant.5. The method of claim 3, wherein the second proppant stage contains aULW proppant.
 6. The method of claim 1, wherein the second proppantstage contains a ULW proppant and further wherein the first proppantstage contains sand, ceramic, sintered bauxite or a resin coatedproppant.
 7. The method of claim 1, wherein the density of the ULWproppant in the first proppant stage and/or second proppant stage isless than or equal to 2.25 g/cc.
 8. The method of claim 7, wherein thedensity of the ULW proppant in the first proppant stage and/or secondproppant stage is less than or equal to 2.0 g/cc.
 9. The method of claim8, wherein the density of the ULW proppant in the first proppant stageand/or second proppant stage is less than or equal to 1.75 g/cc.
 10. Themethod of claim 9, wherein the density of the ULW proppant in the firstproppant stage and/or second proppant stage is less than or equal to1.25 g/cc.
 11. The method of claim 1, which further comprisesintroducing a third proppant stage into the fracture, wherein at leastone of the following conditions prevails: (i.) the rate of injection ofthe third proppant stage into the fracture is different than the rate ofinjection of the second proppant stage; (ii.) the density of the thirdproppant stage is greater than or equal to 0.2 g/cc the density of thesecond proppant stage; or (iii.) the particle size of the proppant ofthe third proppant stage is different from the particle size of theproppant of the second proppant stage.
 12. The method of claim 1,wherein the density differential between the first proppant stage andthe second proppant stage is greater than or equal to 0.2 g/cc andeither the first proppant stage and/or the second proppant stagecontains an ULW proppant.
 13. The method of claim 12, wherein thedensity of the ULW proppant is less than or equal to 2.35 g/cc.
 14. Themethod of claim 13, wherein the density of the ULW proppant is less thanor equal to 2.0 g/cc.
 15. The method of claim 14, wherein the density ofthe ULW proppant is less than or equal to 1.75 g/cc.
 16. A method ofhydraulically fracturing a hydrocarbon-bearing subterranean formationwhich comprises pumping a first proppant stage either into a propagatedfracture or into the formation at a pressure sufficient to fracture theformation and pumping a second proppant stage into the fracture, whereinthe proppant of the first proppant stage and/or the proppant of thesecond proppant stage contains an ultra lightweight (ULW) proppant andfurther wherein the density differential between the proppant of thefirst proppant stage and the proppant of the second proppant stage isgreater than or equal to 0.2 g/cc.
 17. The method of claim 16, whereinthe effective propped length of the fracture after pumping of the secondproppant stage is greater than the effective propped length of thefracture prior to the injection of the second proppant stage.
 18. Themethod of claim 16, wherein the density of the ULW proppant in the firstproppant stage and/or second proppant stage is less than or equal to2.25 g/cc.
 19. The method of claim 18, wherein the density of the ULWproppant in the first proppant stage and/or second proppant stage isless than or equal to 2.0 g/cc.
 20. The method of claim 19, wherein thedensity of the ULW proppant in the first proppant stage and/or secondproppant stage is less than or equal to 1.75 g/cc.
 21. The method ofclaim 20, wherein the density of the ULW proppant in the first proppantstage and/or second proppant stage is less than or equal to 1.25 g/cc.22. A method of hydraulically fracturing a hydrocarbon-bearingsubterranean formation which comprises introducing a first proppantstage into the formation at a pressure sufficient to propagate afracture or into a propagated fracture, wherein the first proppant stagecomprises a first proppant and a second proppant, wherein the firstproppant and/or second proppant is an ultra lightweight (ULW) proppanthaving a density less than or equal to 2.45 g/cc.
 23. The method ofclaim 22, wherein the density differential between the first proppantand the second proppant is about 0.2 g/cc.
 24. The method of claim 23,wherein the density of the ULW proppant is less than or equal to 1.75g/cc.
 25. The method of claim 24, wherein the density of the ULWproppant is less than or equal to 1.25 g/cc.
 26. The method of claim 22,further comprising injecting a second proppant stage into thesubterranean formation, wherein at least one of the following conditionsprevails: (i.) the second proppant stage contains a first proppant and asecond proppant wherein at least one of the first proppant and secondproppant is a ULW proppant; (ii.) the proppant of the second proppantstage is a ULW proppant and the density differential of the firstproppant stage and the second proppant stage is greater than or equal to0.2 g/cc; (iii.) the rate of injection of the second proppant stage intothe fracture is different from the rate of injection of the firstproppant stage; or (iv.) the particle size of the proppant of the secondproppant stage is different from the particle size of the proppant ofthe first proppant stage.
 27. The method of claim 26, wherein theproppant of the second proppant stage is a ULW proppant and the densitydifferential between the first proppant stage and the second proppantstage is greater than or equal to 0.2 g/cc.
 28. The method of claim 26,wherein the proppant of the second proppant stage is a ULW proppant andthe rate of injection of the second proppant stage is less than the rateof injection of the first proppant stage.
 29. The method of claim 26,wherein the proppant of the second proppant stage is a ULW proppant andthe particle size of the proppant of the second proppant stage isgreater than the particle size of the proppant of the first proppantstage.
 30. The method of claim 26, wherein the density differentialbetween the first proppant stage and the second proppant stage isgreater than or equal to 0.2 g/cc and further wherein the secondproppant stage contains a first proppant and a second proppant, thedensity differential of the first proppant and the second proppant ofthe second proppant stage being greater than or equal to 0.2 g/cc. 31.The method of claim 26, wherein the density of the ULW proppant of thesecond proppant stage is less than or equal to 2.0 g/cc.
 32. The methodof claim 22, wherein the first proppant stage is a pad fluid and isintroduced into the formation at a pressure sufficient to initiate afracture.
 33. A method of hydraulically fracturing a hydrocarbon-bearingsubterranean formation which comprises: (a.) introducing into theformation at a pressure sufficient to propagate a fracture or into apropagated fracture a first proppant stage comprising a proppant havinga density greater than 2.45 g/cc; and (b.) introducing into theformation a second proppant stage, comprising an ultra lightweight (ULW)proppant having a density less than or equal to 2.45 g/cc.
 34. Themethod of claim 33, wherein the density differential of the firstproppant stage and the second proppant stage is greater than or equal to0.2 g/cc.
 35. The method of claim 33, wherein the rate of injection ofthe second proppant stage into the fracture is different from the rateof injection of the first proppant stage.
 36. The method of claim 33,wherein the particle size of the proppant of the second proppant stageis different from the particle size of the proppant of the firstproppant stage.
 37. The method of claim 33, wherein the second proppantstage contains a first proppant and a second proppant wherein thedensity differential of the first proppant and the second proppant isgreater than or equal to 0.2 g/cc.
 38. The method of claim 33, whereinthe density of the ULW proppant of the second proppant stage is lessthan or equal to 2.25 g/cc.
 39. The method of claim 38, wherein thedensity of the ULW proppant of the second proppant stage is less than orequal to 2.0 g/cc.
 40. The method of claim 33, wherein the firstproppant stage is a pad fluid and is introduced into the formation at apressure sufficient to initiate a fracture.
 41. A method of fracturing asubterranean formation comprising: pumping a pad fluid containing afirst proppant stage into the formation at a pressure sufficient toinitiate a fracture; injecting a second proppant stage into thefracture, wherein the first proppant stage, and optionally the secondproppant stage, contains an ultra lightweight (ULW) proppant having adensity less than or equal to 2.45 g/cc.
 42. The method of claim 41,wherein the density differential between the proppant of the firstproppant stage in the pad fluid and the proppant of the second proppantstage is at least 0.2 g/cc.
 43. The method of claim 42, wherein thesecond proppant stage has a density greater than 2.45 g/cc.
 44. Themethod of claim 43, wherein the second proppant stage contains sand,ceramic, sintered bauxite or resin coated proppant.
 45. The method ofclaim 41, wherein the second proppant stage contains a ULW proppanthaving a density less than or equal to 2.45 g/cc.
 46. The method ofclaim 45, wherein the density of the ULW proppant is less than or equalto 1.75 g/cc.
 47. The method of claim 46, wherein the density of the ULWproppant is less than or equal to 1.25 g/cc.
 48. The method of claim 41,wherein the effective propped length of the fracture after injection ofthe second proppant stage is greater than the effective propped lengthof the fracture prior to the injection of the second proppant stage. 49.The method of claim 41, which further comprises introducing a thirdproppant stage into the fracture, wherein at least one of the followingconditions prevails: (a.) the density differential of the proppant inthe third proppant stage and the proppant of the second proppant stageis greater than or equal to 0.2 g/cc; (b.) the rate of injection of thethird proppant stage is less than the rate of injection of the secondproppant stage; or (c.) the particle size of the third proppant stage isdifferent from the particle size of the second proppant stage.
 50. Themethod of claim 49, wherein the effective propped length of the fractureafter injection of the third proppant stage is greater than theeffective propped length of the fracture prior to the introduction ofthe third proppant stage.
 51. The method of claim 1, wherein the rate ofinjection of the second proppant stage into the fracture is differentfrom the rate of injection of the first proppant stage and furtherwherein the first proppant stage and/or second proppant stage containsan ultra lightweight (ULW) proppant having a density less than or equalto 2.45 g/cc.
 52. The method of claim 51, wherein the proppant of thefirst proppant stage and/or the second proppant stage contains a ULWproppant and the rate of injection of the second proppant stage is lessthan the rate of injection of the first proppant stage.
 53. The methodof claim 51, wherein the first proppant stage is a pad fluid and isintroduced into the formation at a pressure sufficient to initiate afracture.
 54. A method of hydraulically fracturing a hydrocarbon-bearingsubterranean formation which comprises introducing into a formation afirst proppant stage and a second proppant stage, wherein each of thefirst proppant stage and second proppant stage contains an ultralightweight (ULW) proppant having a density less than or equal to 2.45g/cc and further wherein the ULW proppant of the first proppant stageand/or the second proppant stage is other than ground or crushed shellsof nuts, ground or crushed seed shells of seeds of fruits, ground orcrushed seed shells of plants crushed fruits pits or processed woodmaterials and is capable of withstanding closure stresses greater thanabout 1500 psi at a temperature greater than 150° F.
 55. The method ofclaim 54, wherein the density differential between the first proppantstage and the second proppant stage is greater than or equal to 0.2g/cc.
 56. The method of claim 54, wherein the first proppant stage is apad fluid.
 57. The method of claim 54, wherein the first proppant stageis a banking fluid.
 58. The method of claim 54, wherein the rate ofinjection of the second proppant stage is different from the rate ofinjection of the first proppant stage.
 59. The method of claim 58,wherein the rate of injection of the second proppant stage is less thanthe rate of injection of the first proppant stage.
 60. The method ofclaim 54, wherein the particle size of the proppant of the secondproppant stage is different from the particle size of the proppant ofthe first proppant stage.
 61. The method of claim 60, wherein theparticle size of the proppant of the second proppant stage is greaterthan the particle size of the proppant of the first proppant stage. 62.The method of claim 54, wherein the effective propped length of thefracture after injection of the second proppant stage is greater thanthe effective propped length of the fracture prior to the injection ofthe second proppant stage.
 63. The method of claim 54, wherein thedensity of the ULW proppant of the first proppant stage and/or secondproppant stage is less than or equal to 1.75 g/cc.
 64. The method ofclaim 63, wherein the density of the ULW proppant of the first proppantstage and/or second proppant stage is less than or equal to 1.25 g/cc.65. The method of claim 54, wherein each of the first proppant stage andsecond proppant stage contains an ultra lightweight (ULW) proppanthaving a density less than or equal to 2.45 g/cc and further wherein theULW proppant of the first proppant stage and the second proppant stageis other than ground or crushed shells of nuts, ground or crushed seedshells of seeds of fruits, ground or crushed seed shells of plants,crushed fruits pits or processed wood materials and is capable ofwithstanding closure stresses greater than about 1500 psi at atemperature greater than 150° F.
 66. A method of fracturing asubterranean formation comprising: creating a fracture in the formationby injecting a banking fluid containing a first proppant stage into theformation at pressure sufficient to allow formation of a proppant bank;injecting a second proppant stage into the fracture wherein the densitydifferential between the proppant of the first proppant stage in thebanking fluid and the proppant of the second proppant stage is at least0.2 g/cc; and further wherein the proppant of either the first proppantstage or the second proppant stage is an ultra lightweight (ULW)proppant having a density less than or equal to 2.45 g/cc.
 67. Themethod of claim 66, wherein the effective propped length of the fractureafter injection of the second proppant stage is greater than theeffective propped length of the fracture prior to the injection of thesecond proppant stage.
 68. The method of claim 66, which furthercomprises introducing a third proppant stage into the fracture, whereinat least one of the following conditions prevails: (a.) the densitydifferential of the proppant in the third proppant stage and theproppant of the second proppant stage is greater than or equal to 0.2g/cc; (b.) the rate of injection of the third proppant stage is lessthan the rate of injection of the second proppant stage; or (c.) theparticle size of the proppant of the third proppant stage is differentfrom the particle size of the proppant of the second proppant stage. 69.The method of claim 66, wherein the density of the ULW proppant is lessthan or equal to 1.75 g/cc.
 70. The method of claim 66, wherein theeffective propped length of the fracture after injection of the thirdproppant stage is greater than the effective propped length of thefracture prior to the introduction of the third proppant stage.
 71. Amethod of hydraulically fracturing a hydrocarbon-bearing subterraneanformation which comprises pumping a first proppant stage either into apropagated fracture or into the formation at a pressure sufficient tofracture the formation and pumping a second proppant stage into thefracture, wherein the proppant of the first proppant stage and/or thesecond proppant stage contains a ULW proppant and the particle size ofthe proppant of the second proppant stage is different from the particlesize of the proppant of the first proppant stage.
 72. The method ofclaim 71, wherein the proppant of the first proppant stage and/or thesecond proppant stage contains a ULW proppant and the particle size ofthe proppant of the second proppant stage is greater than the particlesize of the proppant of the first proppant stage.
 73. A method ofhydraulically fracturing a hydrocarbon-bearing subterranean formationwhich comprises: (a.) introducing into the formation at a pressuresufficient to propagate a fracture or into a propagated fracture a firstproppant stage comprising a proppant having a density less than 2.45g/cc; and (b.) introducing into the formation a second proppant stage,comprising an ultra lightweight (ULW) proppant having a density lessthan or equal to 2.45 g/cc.